Abstract
The objective of this study was to evaluate the potential use of wood shavings as a raw material for the low consistency (LC) refining at the primary refining stage to significantly reduce electrical energy consumption. It was possible to produce wood shavings with longer fibre length than wood chips. Oxalic acid, followed by alkaline peroxide, was applied to both wood shavings and wood chips before LC refining. LC refined wood shavings were found to be a low energy raw material. The refining energy was reduced by about 33% using wood shavings compared to wood chips at a given freeness, and oxalic acid pretreatment of wood shavings further reduced the refining energy by approximately 57%. Tensile strength and brightness of LC refined wood shavings was found to be higher than high-consistency refined wood chips. Oxalic acid pretreatment further improved the tensile strength of LC refined wood shavings, but not the brightness. This study demonstrates the potential to develop a novel mechanical pulping process that produces high tensile, high brightness pulp with half the electrical energy consumption. Both wood chips and wood shavings produced in the laboratory were used as a feeding material in HC and LC refining processes, respectively. Fibre length of wood shavings was longer than that of wood chips. As refining proceeded, fibre length of LC refined wood shavings was reduced more than that of HC refined wood chips. Oxalic acid pretreatment further reduced the fibre length of LC refined wood shavings. A great advantage of using wood shavings was found in reducing refining energy over wood chips. LC refined wood shavings reduced the refining energy about 33% compared to HC refined wood chips at a given freeness. Oxalic acid followed by alkaline peroxide pretreatment of wood shavings further reduced refining energy by approximately 57%.,Peer reviewed,Published.